2017 Aluminum Rods

Name:	2017 Aluminum Rods

Aviation High Strength Aluminum Alloy
Aluminum rod: Ordinary aluminum rods, Fine drawn aluminum rods, Polished rods, Aluminum forgings...
Supply status: T4, T3, T351, T451, H112, O...
Round rod: Φ3mm~600mm
Square rod: height 3~200mm* width 10~500mm
Hexagonal bar: S=6~50mm (opposite side)

Product Description

2017 Aluminum Alloy Plate, Pipes, Tubes, Rods, Profiles and Fabrications

SaTraD Group – China’s Top leading steel, metal & raw material distributor.

2017 aluminum alloy has high strength and good cutting performance, but poor corrosion resistance. The 2XXX series aluminum plate is characterized by high hardness, with the highest content of copper, which is about 3-5%. Belongs to aviation aluminum. Usually used for rivets, general machinery parts, aircraft, ships, transportation structures, transportation tool structures, propeller components and accessories.

Specification of 2017 Aluminum Alloy

Material Grade	1050、1060、2A12、2024、2017、LY12、3003、3A21、LF21、5052、5083、5A02、5A05、5A06、LF2、LF5、LF6、6061、6063、6082、7075、7050、7A04、7A09、LC4、LC9, etc.
Color	Nature, silver, bronze, champagne, black, gloden, etc. As customized
Standard	DIN GB ISO JIS ASTM
Thickness	1-100mm
Outer Diameter	6-626mm
Surface Treatment	Mill finish, Anodized, Electrophoresis, Powder coating, Wooden grain, Sand blast

Chemical Composition of 2017 Aluminum Alloy

Alloy Grade	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Zr	Al
2017	0.2-0.8	0.70	3.5-4.5	0.4-1.0	0.4-0.8	0.10	0.25	0.15	-	Balance

Mechanical & Physical Properties of 2017 Aluminum Alloy

Material Grade

Tensile Strength

Yield Strength

Elongation

Hardness

Thermal

Expansion

Melting point

Conductivity

20℃（68℉）

Resistivity 20℃（68℉）

Density

Rm/Mpa

Rp0.2/Mpa

HBWα

200-100 ℃μm/mk

℃

（%IACS）

68℉ Ωmm²/m

20℃g/cm³

2017-T4

390

245

115

23.6

513-640

0.05

2.8

Typical use of 2 series aluminum alloy

2XXX Series	Application Area
2011	Screws and machined products requiring good cutting performance
2014	Occasions requiring high strength and hardness (including high temperature). Aircraft heavy, forgings, thick plates and extruded materials, wheels and structural elements, multi-stage rocket stage fuel tanks and spacecraft parts, truck frames and suspension system parts
2017	2017 is a 2XXX series alloy that has obtained industrial applications. The current application range is relatively narrow, mainly for rivets, general mechanical parts, structural and transportation structural parts, propellers and accessories
2024	Aircraft structure, rivets, truck wheel hubs, propeller components and various other structural parts
2036	Car body sheet metal parts
2048	Aerospace Vehicle Structural Parts and Weapon Structural Parts
2A01	Structural rivets with working temperature less than or equal to 100℃
2A02	Axial compressor blade of turbojet engine with working temperature of 200~300℃
2A06	Rivets for aircraft structures with operating temperature of 150~250℃ and aircraft structures with operating temperature of 125~250℃
2A10	The strength of 2A10 is higher than that of 2A01 alloy. It is used to manufacture aircraft structural rivets whose working temperature is less than or equal to 100℃
2A11	Medium-strength structural parts of aircraft, propeller blades, transportation vehicles and building structural parts. Medium-strength bolts and rivets for aircraft
2A12	Aircraft skins, bulkheads, wing ribs, wing beams, rivets, etc., structural parts of construction and transportation vehicles
2A14	Free forgings and die forgings with complex shapes
2A16	Aerospace aircraft parts with working temperature of 250~300℃, welding container and air-tight cockpit working at room temperature and high temperature
2A17	Aircraft parts with operating temperature of 225~250℃
2A50	Medium-strength parts with complex shapes
2A60	Aircraft engine compressor wheel, wind guide wheel, fan, impeller, etc.
2A70	Aircraft skin, aircraft engine pistons, wind deflectors, etc.
2A80	Aircraft engine compressor blades, impellers, pistons, expansion rings and other parts with high working temperature