5083 Aluminum Coils

Name:	5083 Aluminum Coils

Category: Super anti-rust aluminum alloy
Supply status: H111, H112, H116, H321, O...
Thickness: 0.5mm-6mm
Width: 1250/1500/2000/2200mm
Length: 2500/3000/4000/6000/8000mm

Product Description

5083 Aluminum Alloy Plate, Pipes, Tubes, Rods, Profiles and Fabrications

SaTraD Group – China’s Top leading steel, metal & raw material distributor.

5083 known as Al-Mg-Si series alloy with a wide range of applications. It has good corrosion resistance, excellent weldability, good cold workability, and medium strength.

Used in the manufacture of aircraft fuel tanks, fuel pipes, sheet metal parts of transportation vehicles, ships, instruments, street lamp brackets and rivets, hardware products, electrical enclosures, etc.

Applications

5083 aluminum alloy is commonly used in vessels, vehicle materials, automobile and aircraft plate welding parts, pressure vessels that require strict fire protection, refrigeration devices, TV towers, drilling equipment, transportation equipment, missile components, armor, etc..

Specification of 5083 Aluminum Alloy

Material Grade	1050、1060、2A12、2024、2017、LY12、3003、3A21、LF21、5052、5083、5A02、5A05、5A06、LF2、LF5、LF6、6061、6063、6082、7075、7050、7A04、7A09、LC4、LC9, etc.
Color	Nature, silver, bronze, champagne, black, gloden, etc. As customized
Standard	DIN GB ISO JIS ASTM
Thickness	1mm-290mm
Width/Length	Width: 1250/1500mm Length: 2500/3000/4000mm
Surface Treatment	Mill finish, Anodized, Electrophoresis, Powder coating, Wooden grain, Sand blast
Typical Use	commonly used in vessels, vehicle materials, automobile and aircraft plate welding parts, pressure vessels that require strict fire protection, refrigeration devices, TV towers, drilling equipment, transportation equipment, missile components, armor, etc..

Chemical Composition of 5083 Aluminum Alloy

Alloy Grade	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Zr	Al
5083	0.40	0.40	0.10	0.4-1.0	4.0-4.9	0.05-0.25	0.25	0.15	-	Balance

Mechanical & Physical Properties of 5083 Aluminum Alloy

Material Grade	Tensile Strength	Yield Strength	Elongation	Hardness	Thermal Expansion	Melting point	Conductivity 20℃（68℉）	Resistivity 20℃（68℉）	Density 20℃
	Rm/Mpa	Rp0.2/Mpa	%	HBWα	200-100 ℃μm/mk	℃	（%IACS）	Ωmm²/m	g/cm³
5083-H112	275	125	10	75	24.2	674-638	29	0.0595	2.75
Material Grade	Tensile Strength	Yield Strength	Elongation	Hardness	ThermalExpansion	Melting point	Conductivity 20℃（68℉）	Resistivity 20℃（68℉）	Density 20℃
	Rm/Mpa	Rp0.2/Mpa	%	HBWα	200-100 ℃μm/mk	℃	（%IACS）	Ωmm²/m	g/cm³
5083-O	270-350	125	11	75	24.2	574-638	29	0.0595	2.75