5A02 Aluminum Plates

Name:	5A02 Aluminum Plates

Category: Super anti-rust aluminum alloy
Type: bright aluminum plate, brushed aluminum plate, film aluminum plate, pattern aluminum plate, super flat aluminum plate...
Supply status: H32, H24, H22, H112, O...
Thickness: 0.5mm-150mm
Width: 1250/1500/2000mm
Length: 2500/3000/4000/6000mm

Product Description

5A02 Aluminum Alloy Plate, Pipes, Tubes, Rods, Profiles and Fabrications

SaTraD Group – China’s Top leading steel, metal & raw material distributor.

5A02 is known as Al-Mg series rust-proof aluminum alloy. The alloy has low magnesium content, high plasticity, good forming ability and low strength. However, it is stronger than 3A21 alloy. Cold deformation can increase its strength, while plasticity decreases. Besides, 5A02 aluminum alloy has good corrosion resistance and is suitable for use in marine environments. Also well known as good weldability. The machinability is poor in the annealed state, and the semi-cold work hardening state can improve the machinability.

Applications

5A02 aluminum alloy is suitable for welding structures and containers with high process plasticity requirements and good corrosion resistance, such as fuel tanks, gasoline and lubricating oil pipes, flanges and light-loaded parts, marine, vehicle interior decoration parts, etc. Wire rods aluminum are used as rivets or welding rods.

Specification of 5A02 Aluminum Alloy

Material Grade	1050、1060、2A12、2024、2017、LY12、3003、3A21、LF21、5052、5083、5A02、5A05、5A06、LF2、LF5、LF6、6061、6063、6082、7075、7050、7A04、7A09、LC4、LC9, etc.
Color	Nature, silver, bronze, champagne, black, gloden, etc. As customized
Standard	DIN GB ISO JIS ASTM
Thickness	Thickness: 0.5mm-150mm
	Width: 1250/1500/2000mm Length: 2500/3000/4000/6000mm
Surface Treatment	Mill finish, Anodized, Electrophoresis, Powder coating, Wooden grain, Sand blast
Typical Use	commonly used in the manufacturer of armor plate, high strength structural parts, storage tanks, pressure vessels and parts of marine products

Chemical Composition of 5A02 Aluminum Alloy

Alloy Grade	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Zr	Al
5A02	0.40	0.40	0.10	0.15-0.4	2.0-2.8	-	-	0.15	-	Balance

Mechanical & Physical Properties of 5A02 Aluminum Alloy

Material Grade

Tensile Strength

Yield Strength

Elongation

Hardness

Thermal

Expansion

Melting point

Conductivity

20℃（68℉）

Resistivity 20℃（68℉）

Density

20℃

Rm/Mpa

Rp0.2/Mpa

HBWα

200-100 ℃μm/mk

℃

（%IACS）

Ωmm²/m

g/cm³

5A02-H32

210-260

130

23.8

607-649

0.0493

2.73