5754 Aluminum Plates

Name:	5754 Aluminum Plates

Category: Super anti-rust aluminum alloy
Supply status: H111, H112, H22, H24, O...
Thickness: 0.2mm-6mm
Width: 1250/1500/2000/2200mm
Length: 2500/3000/4000/6000/8000mm

Product Description

5754 Aluminum Alloy Plate, Pipes, Tubes, Rods, Profiles and Fabrications

SaTraD Group – China’s Top leading steel, metal & raw material distributor.

5754 belongs to AL-MG anti-rust aluminum. It has the characteristics of medium strength, good corrosion resistance, weldability and easy processing and forming. It is a typical alloy among Al-Mg alloys. 5754 in different heat treatment states is the main material used in the automobile manufacturing industry (car doors, molds, seals) and canning industry.

Applications

5754 is widely used in auto parts, welded structures, storage tanks, pressure vessels, trains, ship structures and offshore facilities, transportation tanks and tanks that require excellent processing performance, excellent corrosion resistance, high fatigue strength, and high weldability and occasions of medium static strength.

Specification of 5754 Aluminum Alloy

Material Grade	1050、1060、2A12、2024、2017、LY12、3003、3A21、LF21、5052、5083、5A02、5A05、5A06、LF2、LF5、LF6、6061、6063、6082、7075、7050、7A04、7A09、LC4、LC9, etc.
Color	Nature, silver, bronze, champagne, black, gloden, etc. As customized
Standard	DIN GB ISO JIS ASTM
Thickness	1mm-290mm
Width/Length	Width: 1250/1500mm Length: 2500/3000/4000mm
Surface Treatment	Mill finish, Anodized, Electrophoresis, Powder coating, Wooden grain, Sand blast
Typical Use	commonly used in vessels, vehicle materials, automobile and aircraft plate welding parts, pressure vessels that require strict fire protection, refrigeration devices, TV towers, drilling equipment, transportation equipment, missile components, armor, etc..

Chemical Composition of 5754 Aluminum Alloy

Alloy Grade	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Zr	Al
50754	0.40	0.40	0.10	0.50	2.6-3.6	0.30	0.20	0.15	-	Balance

Mechanical & Physical Properties of 5754 Aluminum Alloy

Material Grade

Tensile Strength

Yield Strength

Elongation

Hardness

Thermal

Expansion

Melting point

Conductivity

20℃（68℉）

Resistivity 20℃（68℉）

Density

20℃

Rm/Mpa

Rp0.2/Mpa

HBWα

200-100 ℃μm/mk

℃

（%IACS）

Ωmm²/m

g/cm³

57543-H111

190-240

23.7

602-646

0.051

2.73